Table 6 Tested bacteria inoculum density (CFU/mL) reduction on Cu-ETP, CuSn6, CuZn37, CuNi18Zn20, stainless steel, in chosen time periods

From: Antibiotic resistance, ability to form biofilm and susceptibility to copper alloys of selected staphylococcal strains isolated from touch surfaces in Polish hospital wards

Time [min]

MSSE 65a

MRSE 62

MSSH 93

MRSH 89

SA

Cu-ETP

 0

1.25E + 06

1.38E + 06

4.22E + 06

4.52E + 06

7.49E + 06

 30

4.83E + 05

4.67E + 05

7.50E + 05

1.68E + 06

2.33E + 06

 60

1.00E + 05

3.50E + 03

3.33E + 04

8.60E + 05

7.92E + 05

 90

8.50E + 03

4.17E + 03

1.67E + 05

3.73E + 04

3.87E + 05

 120

1.00E + 00

1.00E + 00

8.33E + 05

1.00E + 00

4.67E + 04

 180

1.00E + 00

1.00E + 00

1.67E + 05

1.00E + 00

1.00E + 04

 240

1.00E + 00

1.00E + 00

1.00E + 00

1.00E + 00

1.00E + 00

 300

1.00E + 00

1.00E + 00

1.00E + 00

1.00E + 00

1.00E + 00

CuSn6

Time [min]

MSSE 65

MRSE 62

MSSH 93

MRSH 89

SA

 0

4.43E + 06

1.73E + 06

5.05E + 06

2.68E + 06

1.13E + 07

 30

5.17E + 05

9.00E + 05

2.35E + 06

1.23E + 06

4.33E + 05

 60

1.00E + 05

3.00E + 05

1.23E + 06

1.32E + 05

3.08E + 03

 90

4.50E + 04

1.67E + 04

1.72E + 05

3.90E + 05

1.17E + 03

 120

1.50E + 04

3.00E + 04

2.48E + 05

9.67E + 04

1.00E + 00

 180

5.00E + 03

2.17E + 04

6.37E + 05

1.17E + 04

1.00E + 00

 240

1.67E + 03

1.00E + 00

5.83E + 04

1.67E + 03

1.00E + 00

 300

1.00E + 00

1.00E + 00

1.00E + 00

1.10E + 05

1.00E + 00

CuZn37

Time [min]

MSSE 65

MRSE 62

MSSH 93

MRSH 89

SA

 0

5.62E + 06

4.17E + 06

6.17E + 06

1.68E + 06

1.01E + 07

 30

1.25E + 06

1.43E + 06

6.38E + 06

1.13E + 06

6.55E + 06

 60

1.72E + 06

5.83E + 05

2.83E + 06

1.25E + 06

2.78E + 06

 90

7.33E + 05

6.67E + 04

3.67E + 05

8.50E + 05

1.47E + 05

 120

3.02E + 05

4.00E + 04

5.00E + 05

5.25E + 05

3.97E + 05

 180

6.33E + 04

1.67E + 04

1.83E + 05

1.88E + 05

7.10E + 05

 240

1.30E + 05

8.33E + 03

1.92E + 05

1.68E + 05

4.70E + 05

 300

6.67E + 03

3.33E + 04

3.17E + 04

1.72E + 05

6.50E + 04

CuNi18Zn20

Time [min]

MSSE 65

MRSE 62

MSSH 93

MRSH 89

SA

 0

1.05E + 06

1.17E + 06

2.45E + 06

4.25E + 05

9.20E + 06

 30

9.17E + 05

3.68E + 06

2.18E + 06

2.25E + 05

6.77E + 06

 60

5.67E + 05

5.67E + 05

1.23E + 05

3.63E + 05

2.70E + 06

 90

4.83E + 04

3.67E + 04

5.00E + 03

5.33E + 04

1.50E + 06

 120

4.50E + 04

3.00E + 04

1.00E + 00

3.52E + 05

2.38E + 05

 180

2.00E + 04

3.67E + 04

1.00E + 00

1.83E + 04

2.12E + 05

 240

5.00E + 03

8.33E + 03

1.00E + 00

1.67E + 04

5.77E + 05

 300

1.67E + 03

1.00E + 00

1.00E + 00

2.50E + 04

2.83E + 03

SS

Time [min]

MSSE 65

MRSE 62

MSSH 93

MRSH 89

SA

 0

1.05E + 06

8.17E + 06

2.98E + 06

3.33E + 06

1.18E + 07

 30

9.83E + 05

3.40E + 06

2.87E + 06

2.20E + 06

1.20E + 07

 60

8.00E + 05

1.43E + 06

2.45E + 06

4.63E + 06

1.27E + 07

 90

7.00E + 05

2.02E + 06

2.22E + 06

1.80E + 06

1.25E + 07

 120

7.33E + 05

1.23E + 06

2.12E + 06

2.10E + 06

1.30E + 07

 180

1.55E + 06

1.80E + 06

1.73E + 06

3.43E + 06

1.05E + 07

 240

9.67E + 05

1.92E + 06

3.20E + 06

1.50E + 06

9.33E + 06

 300

9.50E + 05

1.50E + 06

5.15E + 06

3.08E + 06

9.77E + 06

  1. astrains codes – see Table 3